Applications
High transparency heat shrinkable tube, manufactured by coextrusion polyolefin and
polyamide, it has excellent tensile strength, puncture resistance and waterproof properties.
Especially designed for environmental sealing and protection of crimp splices and
terminations.
Features
Shrink ratio: 3:1
Abrasion and corrosion resistance
Water proof and moisture resistance
Highly translucence and elasticity.
Various
Operating temperature : -45°C~105°C
Minimum fully recovery temperature: 100°C
Standard color: Red, Blue, Yellow

Technical Data

Property	Test Method	Values
Tensile strength	Room temp	≥16  MPa
Elongation at break		≥200%
Voltage withstand and breakdown Voltage		Withstand 2.5KV for 1minute and breakdown
Tensile strength at aging	150°C/7days	≥11.5 MPa
Elongation at break at aging		≥100%
Voltage withstand and breakdown Voltage at aging		At least half of un-aged breakdown voltage
Copper   corrosion		No sign of degradation
Copper stability		No drop, no flow
Cold  bend	-40°C/4 hrs	No  cracking
Maximum  secant  modulus   (2%)		250MPa
Volume resistivity		Min.1014 Ω·cm
Heat  shock	200°C/4 hrs	No  cracking

Dimensions

As Supplied (mm)		After Recovery (mm)		Standard length
Inside Diameter    Min. (D)	Wall Thickness Min. (WT)	Inside Diameter Min. (D)	Wall Thickness   Min. (WT)	m/roll
Φ4.8±0.3	0.50±0.05	Φ1.4	1.2±0.1	100
Φ5.8±0.3	0.50±0.05	Φ1.7	1.3±0.1	100
Φ6.8±0.3	0.70±0.05	Φ2.1	1.5±0.1	100
Φ7.0±0.3	0.50±0.05	Φ2.5	1.5±0.1	100
Φ8.3±0.3	0.65±0.05	Φ3.0	1.65±0.1	100